EPOFLOOR SELF LEVELLING MORTAR
Up to 1-3 cm thickness
Product description
Cement-based monocomponent flooring mixture, rich in chemical mixtures, providing formation of imporous surface. It is levelled in a self-spreading manner.
The product conforms to the requirements of the AZS 039-2000 (TS 11140-1993) standard.
Fields of Application
This product can be applied in the following areas:
Formation of flat surface before application of different materials, such as wood, laminate, parquet, carpet, PVC, ceramics;
Formation of strong surface resistant to erosion and dust in storages and similar facilities;
Advantages
Easily prepared and used;
Creates flat, imporous surface in a self-levelling manner.
Preparation of surface. Please pay attention to the surface to be checked and strong and removed of residues preventing adhesion. In case the surface has cracks or pores, they should be filled with Eposement repair mortar. The surface should be primed with Epolatex primer to reduce the ability of water absorption of the surface and increase its resistance.
Preparation of mixture. Gently pour out 25 kg dry mixture onto6,0 liter water, and mix until balls and air bubbles disappear (to prepare the mixture it is recommended to use poor circulation mixer).
Application. Pour the prepared liquid mixture onto the surface. To remove air bubbles from the mixture during the application, and facilitate the levelling procedure, use prickly roller. If required, a steel trowel can be used to accelerate levelling. In case it is required to obtain 20,0 mm thickness, the Epofloor product should be applied in 2 layers. The period between the layers may be 60-90-minutes depending on the temperature. The surface applied with the product should be protected from wind and direct sun for 24-hour period.
Recommendations. In case the Epofloor product ambient temperature is within +50C and +300C, a required temperature should be provided. The product should not be used in hot (more than +300C), rainy and windy weather conditions. After use all appliances and tools should be cleaned with water.
Technical specifications
Color |
Grey |
Operating temperature |
+50 C - +300 C |
Water /dry mixture ratio |
5.5-6 l liter of water /25 kg dry mixture |
Useful life |
35 minutes |
Application thickness |
10,0 – 30,0 mm |
Hardening period: initial final |
In 15-30 minutes In 60-90 minutes |
Compression strength limit: in 2 days in 7 days in 28 days |
15,0 MPa 35,0 MPa 40,0 MPa |
Adhesion |
2,0 MPa |
Period of putting into operation |
In 6 hours the surface can be open for movement. In 24 hours carpet, parquet, tiles, etc. can be applied onto the surface. |
Packing |
25 kg sacks made of 2 or 3-layer kraft paper and 1 layer of polyethilene |
Consumption
The product consumption for 1 m2 surface area with 1mm thickness is 1,75 kg.
Shelf Life and storage
The product can be stored during 12 months in dry conditions, with maximum 10 sacks laid one on another.
Warnings
Taking into consideration that the Epofloor product is a cement-based, complex mixture, immediately rinse it with water in case of contact with skin or eyes;
Do not add any substances not indicated in the application procedures;
Specifications indicated above have been received on the basis of laboratory tests conducted in the ambient conditions of +230C±20C temperature and 50% + 5% humidity. Depending on the ambient conditions these specifications may be changed.
Warranty and technical support
Information indicated in the technical specifications is based on scientific and practical knowledge;
“EPO" company is responsible only for the product quality;
Except for the works carried out under the guidance of the company specialists, “EPO" company bears no responsibility for any problems that may occur as a result of improper use of the product by other users;
The company reserves the right to make changes to its product that may occur due to a scientific and technnological development;
For technical support or more information please do not hesitate to contact “EPO" company!
Last Updated (Thursday, 06 October 2016 07:52)